Green synthesis of Iron nanoparticles using an aqueous extract of strawberry (Fragaria × ananassa Duchesne) leaf waste

Abstrakt

n this study, we analysed the potential use of dried strawberry leaves and calyces for the production of nanoparticles using inorganic iron compounds. We used the following iron precursors FeCl3 × 6H2O, FeCl2 × 4H2O, Fe(NO3)3 × 9H2O, Fe2(SO4)3 × H2O, FeSO4 × 7H2O, FeCl3 anhydrous. It was discovered that the content of polyphenols and flavonoids in dried strawberries and their antioxidant activity in DPPH and FRAP were 346.81 µM TE/1 g and 331.71 µM TE/1 g, respectively, and were similar to these of green tea extracts. Microimages made using TEM techniques allowed for the isolation of a few nanoparticles with dimensions ranging from tens of nanometres to several micrometres. The value of the electrokinetic potential in all samples was negative and ranged from −21,300 mV to −11,183 mV. XRF analyses confirmed the presence of iron ranging from 0.13% to 0.92% in the samples with a concentration of 0.01 mol/dm3. FT-IR spectra analyses showed bands characteristic of nanoparticles. In calorimetric measurements, no increase in temperature was observed in any of the tests during exposure to the electromagnetic field. In summary, using the extract from dried strawberry leaves and calyxes as a reagent, we can obtain iron nanoparticles with sizes dependent on the concentration of the precursor.

Autorzy

Elżbieta Grządka
Elżbieta Grządka
Jolanta Orzeł
Jolanta Orzeł
Agnieszka Nawrocka
Agnieszka Nawrocka
artykuł
Materials
Angielski
2024
17
11
2515
otwarte czasopismo
CC BY 4.0 Uznanie autorstwa 4.0
ostateczna wersja opublikowana
w momencie opublikowania
2024-05-23
140
3,1
0
0